سیستم های رنگ بر اساس IPS-E-TP-100

PAINT SYSTEM NO. SURFACE PREPARATION PRIMER COAT
PC INTERMEDIATE COAT
IC TOP COAT
TC MINIMUM DRY FILM THICKNESS
(micron)       GROUP 1 - OIL-BASE PAINT SYSTEMS FOR USE ON SURFACE TEMPERATURES UP TO 80°C             PC IC TC TOTAL     1A ST3 RED LEAD
IPS-M-TP-115 ALKYD PAINT
IPS-M-TP-130 ALKYD PAINT
IPS-M-TP-130 70 40 40 150   * (IPS-M-TP-125) for white
(IPS-M-TP-165) for black
(IPS-M-TP-155) aluminum for intermediate
(IPS-M-TP-150) aluminum (leafing) for top coat
(IPS-M-TP-160) aluminum (high build) thixotropic for top coat 1B ST3 70 50 50 170 1C ST3 70 60 60 190 1D ST3 70 70 70 210 1E ST3 70 80 80 230 1F ST3 70 90 90 250 GROUP 2 - SILICON ALKYD PAINT SYSTEMS FOR USE ON SURFACES UP TO TEMPERATURE 200°C (SEE 8.4.15)   2A SA2 ½ ZINC
SILICATE
(IPS-M-TP-210) OXID
SILICON
(IPS-M-TP-220) SILICON
ALKYD
(IPS-M-TP-175) 70 125 50 245     2B SA2 ½ 70 220 50 340     2C SA2 ½ ACRILIC
(IPS-M-TP-168) 75 25 25 125     GROUP 3 - VINYL PAINT SYSTEMS FOR USE ON SURFACE TEMPERATURES UP TO 80°C               W.PC PC IC TC TOTAL   3A SA2 ½ WASH
PRIMER
IPS-MTP-180 VINYL
REDLEAD
IPS-MTP-185 VINYL
PAINT
(IPS-MTP-200)* VINYL
PAINT
(IPS-MTP-200)* 10 40 25 25 100 * (IPS-M-TP-170) for black 3B SA2 ½ 10 60 25 25 120 3C SA2 ½ 10 70 25 50 155 3D SA2 ½ 10 80 25 50 165 3E SA2 ½ 10 100 50 50 210 GROUP 4 - ORGANIC ZINC-RICH PAINT SYSTEMS FOR USE ON SURFACES UP TO TEMPERATURE 120°C* (SEE 8.4.15)   4A SA3 ZINC-RICH EPOXY
PAINT
(IPS-M-TP-205)             75   MINIMUM
DRY FILM THICKNESS
(MICRONS) 4B SA3             100   4C SA3             150   GROUP 5 - INORGANIC ZINC-RICH PAINT SYSTEMS FOR USE ON DRY SURFACES UP TO TEMPERATURE 400°C* (SEE 8.4.15)   5A SA 3 ZINC-SILICATE
PAINT
(IPS-M-TP-210)             50   * The appearance of zinc-rich coatings are improved by the application of a suitable sealer
coat, guidance on type of top coat to be used should be obtained from the supplier of the
zinc-rich coatings. 5B SA 3             75   5C SA 3             100   5D SA 3             150   GROUP 6 - CHLORINATED RUBBER PAINT SYSTEMS FOR USE ON SURFACE TEMPERATURES UP TO 65°C   6A ST 3 CHLORINATED
RUBBER
INHIBITIVE
(IPS-M-TP-145) CHLORINATED
RUBBER
INTERMEDIATE
(IPS-M-TP-140) CHLORINATED
RUBBER
TOP COAT
(IPS-M-TP-135) 35 100 30 165     6B ST 3 36 100 60 196     6C SA 2 ½ 37 60 60 157     6D SA 2 ½ 38 100 30 168     6E SA 2 ½ 39 100 60 199     6F SA 2 ½ 40 100 100 240     6G SA 2 ½ 41 100 100 241     6H SA 2 ½ ZINC
SILICATE
(IPS-M-TP-210) 42 100 100 242     6I SA 2 ½ 75 200 200 475     GROUP 7 - EPOXY PAINT SYSTEMS FOR USE ON SURFACE TEMPERATURES UP TO 120°C   7A SA 2 ½ EPOXY
POLYAMIDE
(IPS-M-TP-215) EPOXY
POLYAMIDE
(IPS-M-TP-220) EPOXY
POLYAMIDE
(IPS-M-TP-225) 35 100 45 180   * See IPS-E-TP-270
Note:
1) Two-Pack polyurethane paint (IPS-M-TP-235) can also be used as top coat in epoxy paint
systems 7A to 7F instead of epoxy polyamide top coat.
2) Aliphatic urethane topcoats with the thickness of 35-50-micron are recommended where
the highest degree of gloss and color retention, along with chemical resistance and
recoatability, are desired. 7B SA 2 ½ 70 100 70 240   7C SA 2 ½ 70 100 100 270   7D SA 2 ½ 70 150 100 320   7E SA 2 ½ ZINC RICH
EPOXY
(IPS-M-TP-205) 75 80 125 280   7F SA 2 ½ ZINC
SILICATE
(IPS-M-TP-210) 65 80 80 225   7G SA 2 ½ 75 80 125 280   7H SA 2 ½ EPOXY
POLYAMINE
(IPS-M-TP-202) 100 100 100 300   7I SA 2 ½ EPOXY
POLYAMINE
(IPS-M-TP-225) 125 125 125 375   7J SA 2 ½ --- --- 150 150   7K SA 2 ½ COAL TAR
EPOXY
(IPS-M-TP-190) COAL TAR
EPOXY
(IPS-M-TP-190) --- 150 150 300   7L SA 2 ½ COAL TAR
EPOXY
(IPS-M-TP-190) 150 150 150 450   7M* SA 2 ½ EPOXY CLAD --- --- --- 3MM*   GROUP 8 - ZINC COATINGS OTHER THAN SPRAYED SYSTEMS   8A ACCORDING TO
(IPS-C-TP-101) GALVANIZED             85   Arc-Sprayed aluminum for use on surface temperature up to 550°C 8B             100   8C             140   8D             210   GROUP 9 - SPRAYED-METAL COATING SYSTEMS 9A ACCORDING TO
(IPS-C-TP-101)   ALUMINUM           100 MINIMUM
DRY FILM THICKNESS
(MICRONS) 9B             250 9C             250 9D   ZINC           100 9E             150 9F             250 GROUP 10 - COLD APPLIED BITUMEN PAINT SYSTEMS   10A SA 2½ ASPHALT
MASTIC
(IPS-M-TP-105) ASPHALT
MASTIC
(IPS-M-TP-105) ASPHALT
MASTIC
(IPS-M-TP-105) 800 800 800 2400  

1) All materials should be applied in accordance with the manufacturer’s instructions. Care
should be exercised to ensure there is no mixing of material from different sources or of
different types. In particular, it should be recognized that the chemical and physical
characteristics of bitumen-based coatings differ from those of coal-tar-based coatings and
that the two kinds of coating should not be blended in protective coatings. It is also essential
to clear out plant thoroughly when the use of coal-tar coating materials follows that of
bitumen coating materials or vice versa.
2) For application by flooding or other means, the temperature of the coating material should
be such that the Viscosity is controlled to give the thickness of coating required, and not so
high as to cause excessive fuming. No grade of material shall be heated above the maximum
application temperature given by the manufacturer or above 250°C.

 

10B SA 2½ COAL TAR
PRIMER
(IPS-M-TP-280) COAL TAR
PRIMER
(IPS-M-TP-280) COAL TAR
PRIMER
(IPS-M-TP-280) 400 800 800 2000  